Pengaruh Proses Equal Channel Angular Pressing Terhadap Sifat Mekanik Aluminium Silikon Dengan Suhu Anil 300°C

Doni Eka Phutra.D, Yulfitra Yulfitra

Abstract


The aim of this study to study the effect of the Equal Channel Angular Pressing process the mechanical properties of aluminum silicon with annealing temperature of 300 ° C. An aluminum silicon rod with a length of 40 mm and a width of 9.5 mm in diameter is passed to the ECAP mold with a mold flow angle of 120 °. Material hardness and microstructure of materials before and after the ECAP process are examined and compared. The results showed that after the ECAP process, the hardness of aluminum silicon in the longitudinal section increased and was fairly evenly distributed, ie, at annealing time of 10 minutes the hardness value was 54.30 BHN, at 15 minutes resistance the hardness increased to 55.08 BHN and 25 minutes the hardness value rose to 55.69 BHN, as well as the microstructure showed that the longer the time annealed, the finer the grains on silicon aluminum.

Keywords


Aluminum silicon, ECAP, hardness, metallography.

DOI:

https://doi.org/10.30596/rmme.v1i1.2433


Full Text:

PDF

References


Olejnik dan Rosochowski, Material yang berukuran tinggi mampu bentuk yang tinggi tahan korosi dan komposisi kimia yang sederhana, 2005.

Kuswarini, Penghalusan butir material kuningan melalui proses equal channel angular pressing dengan sudut cetakan 120°. Fakultas Teknik. Universitas Indonesia, 2012.

Nugroho Eko, Pengaruh Unsur Aluminium Dalam Kuningan Terhadap Kekerasan, Kekuatan Tarik, dan Struktur Mikro. Fakultas Teknik. Universitas Muhammad Metro, 2011.

Szajnar dan Wrobel, Peningkatan sifat mekanis aluminium diantaranya dengan penambahan paduan Ti-B untuk penghalusan butir, 2007.

Goni dan Equizabal, AlSi8Cu3Fe dengan menambahkan 0,6% TiB2 pada proses HPDC, 2004.

Kashyap, K.T. dan Chandrashekar, T. Effect and mechanisms of grain refinement in aluminium alloys, Bullet Mater Sci, Vol.4 no.4 August. 2001.

Ginting, Penguatan Dengan Penghalusan Butir Pada Paduan Hipoeutektik Al-Si, Buletin IPT NO. III, 1998.

ASM International, Diagram fasa Al-Si, 2004.

ASM International, Kandungan Si terhadap temperatur titik beku paduan aluminium, 2004.

Considin P.E. Douglas M, Sifat-sifat fisik aluminium, 1983.

Van Der Walls, Semakin dekat butir-butir di dalam suatu material maka sifat kekerasan material tersebut semakin meningkat, dalam aditya dkk 2011.


Refbacks

  • There are currently no refbacks.