Karakteristik Sifat Fisis Keramik Berpori Menggunakan Bahan Dasar Cangkang Kepah
Abstract
Research has been carried out which aims to determine the characteristics of porous ceramics with a mixture of Kepah clam shell powder and clay that can be produced and to determine the influence of Kepah clam shells and clay on the characteristics of porous ceramics, as well as knowing the variations in the composition of mixing Kepah clam shell powder and clay to obtain porous ceramics with optimum characteristics. The kepah clam shell material used is kepah clam shell waste that is no longer used. Variations in the mixture of clay, kepah clam shell powder and kaolin include 6 g : 2 g : 2 g, 5.5 g : 2.5 g : 2 g, 5 g : 3 g : 2 g, 4 g : 4 g : 2 g . The test parameters used are density, porosity and absorbability. The test results showed that the density value of sample A was 0.94 g/cm3, sample B was 0.92 g/cm3, sample C was 0.82 g/cm3 and sample D was 0.81 g/cm3. The porosity value in sample A is 14.32%, sample B is 14.64%, sample C is 17.6%, and sample D is 17.95%. The water absorption value in sample A is 17.38%, sample B is 17.77%, sample C is 17.38%, and sample D is 19.16%, reaching the standard value set by SNI 8640:2018, namely the maximum value. 25%.
Keywords
References
Bahar, F, F., Nuklirullah, M., Tamimah, K. N. (2022). Pemanfaatan Tumbukan Cangkang Kerang Sebagai Pengganiti Agregat Kasar Pada Campuran Beton, Jurnal Teknik Sipil Universitas Sultan Ageng, Vol 11 No 2.
Purbaningsih, Y., Helviani, H., Hasbiadi, H., Nursalam, N., Masitah, M., Kasmin, M. O., ... & Amin, M. (2023). Peningkatan Kapasitas Para Pelaku Usaha Mikro Kecil dan Menengah (UMKM) Melalui Pemanfaatan Limbah Cangkang Kerang di Kota Kendari. Jurnal Pengabdian Multidisiplin, 3(2).
Ulfah, M., & Mora, M. (2024). Pengaruh Penambahan Silika (SiO2) dan Suhu Pembakaran Terhadap Karakteristik Keramik Kordierit Berbasis Abu Sekam Padi. Jurnal Fisika Unand, 13(1), 54-60.
Mahfuzin, A. M., Respati, S. M. B., Dzulfikar. M. (2020).Analisis Filter Keramik Berpori Berbasis Zeolit, Jurnal Teknik MesinJurusan Teknik Mesin Universitas Wahid Hasyim Semarang, Vol 16 No 1.
Pratiwi, D., Daulay, A. H., & Jumiati, E. (2022). Analisis Uji Fisis Keramik Berpori Berbahan Clay dan Kulit Kakao. Jurnal Ikatan Alumni Fisika Universitas Negeri Medan, Vol 8 No 4.
Hairunisa. dkk. (2019). Sintesis Kalsium Oksida dari Canngkang Ale-Ale (MeretrixMeretrix) pada Suhu Kalsinasi 700 ̊C. Jurnal Kimia Khatulistiwa, Vol 5 No1
Darmayanti, E., Darmayanti, L., Putri, M., & Hs, E. (2020). Membran Keramik Berbahan Dasar Tanah Liat dan Fly Ash untuk Penyisihan Warna dan Zat Organik pada Air Gambut. Jurnal Rekayasa Sipil Dan Lingkungan.
Putri, S. E., Rahman, A., Pratiwi, D. E., Majid, A. F., & Tjahjanto, R. T. (2021). Analisis Kandungan Oksida Logam Clay Alam Kabupaten Pangkep Provinsi Sulawesi Selatan sebagai Bahan Dasar Pembuatan Keramik Berpori Gelcasting. Fullerene Journal of Chemistry, 6(2), 171-176.
Tendean, M. N. M., Medellu, C., & Tumangkeng, J. (2021). Proses HOTL dalam mengeksplorasi konsep dan proses tentang pembuatan keramik. Charm Sains: Jurnal Pendidikan Fisika, 2(1), 21-27.
Side, S., Putri, S. E., & Magfirah, N. (2021). Efektivitas Katalis Fe2O3 Terimpregnasi dalam Keramik Berpori Gelcasting Pada Proses Fotodegradasi Fenol. Indonesian Journal of Fundamental Sciences Vol, 7(2).
Slamet, S. S. S., Rahmawati, R. R., & Solekhan, S. S. (2023). Diversifikasi Produk Keramik Berpori Sebagai Membran Filtrasi Air Melalui Pelatihan Di KUB Tanah Aji. DHARMA BAKTI, 141-150.
Fadli, M. F., Amirullah, A., Manggala, A., Zurohaina, Z., & Junaidi, R. (2022). Teknologi Pervaporasi Menggunakan Membran Poliamida dalam Menghasilkan Etanol Absolut. Jurnal Pendidikan dan Teknologi Indonesia, 2(3), 109-113.
Pratiwi, D., Daulay, A. H., & Jumiati, E. (2022). Analisis Uji Fisis Keramik Berpori Berbahan Clay dan Kulit Kakao. Jurnal Ikatan Alumni Fisika Universitas Negeri Medan, Vol 8 No 4.
Wibowo, I. A., Sulistyo, S., & Suprihanto, A. (2022). PEMBUATAN ELEKTRODA GRAFIT BERPORI UNTUK PROSES ELEKTROLISIS. JURNAL TEKNIK MESIN, 10(4), 497-502.
Ngurah, A. I. W. A. A., Kristyawan, I. P. A., & Bagus, S. D. I. G. (2024). Pertumbuhan Crustose Coralline Algae (CCA) pada Substrat Keramik dengan Komposisi dan Jenis Material Penyusun yang Berbeda. Jurnal Teknologi Lingkungan, 25(1), 080-087.
DOI: https://doi.org/10.30596/rmme.v7i2.18607
Refbacks
- There are currently no refbacks.
This work is licensed under a Creative Commons Attribution 3.0 License
Jurnal Rekayasa Material, Manufaktur dan Energi is abstracting & indexing in the following databases:
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
Statcounter View My Stats RMME