Sintesis Dan Karakterisasi Kertas Berbahan Dasar Kulit Pisang Kepok Dan Kulit Durian

Adella Ayu Putri Pasaribu; Abdul Halim Daulay; Miftahul Husnah

doi:10.30596/rmme.v8i1.19480

Sintesis Dan Karakterisasi Kertas Berbahan Dasar Kulit Pisang Kepok Dan Kulit Durian

Adella Ayu Putri Pasaribu, Abdul Halim Daulay, Miftahul Husnah

Abstract

Research has been carried out which aims to find out whether paper can be produced from kepok banana peels and durian peels, as well as knowing the characteristics of the paper produced and the optimum variations. The materials used for Kepok banana peels and durian peels are waste from Kepok banana peels and durian peels that are no longer used. Variations in the composition of Kepok banana peel and durian peel used include 30:70 (sample A), 50:50 (sample B), 70:30 (sample C). The characteristics of this research are grammage test, tensile resistance test, tensile strength test, water content test, and (SEM) test. The research results showed that the grammage test results for sample A were 56.66 g/m², sample B was 53.33 g/m², sample C was 50.33 g/m². The tensile resistance test value for sample A is 2.218MPa, sample B is 0.247MPa, sample C is 1.074 MPa. The tensile strength test value for sample A was 0.37%, sample B was 0.29%, and sample C was 0.35%. The water content test value for sample A was 5.1%, sample B was 1.5%, and sample C was 4.3%. The optimum characteristics found in sample A are variations in mixing kepok banana peel and durian peel 30:70.

Keywords

Paper, Durian Skin, Kepok banana skin

Full Text:

PDF

References

Nurisman, E., Emilia, T., Melwita, E., Haryani, N., & Asyeni, M. J. (2021). PELATIHAN DAN PENDAMPINGAN PENGOLAHAN SAMPAH ORGANIK MENJADI KERTAS DAUR ULANG DENGAN ADITIF BAHAN ALAMI. Applicable Innovation of Engineering and Science Research (AVoER), 329-336.

Nurfaridza, R. (2020). Aplikasi Bacterial Cellulose dari Limbah Kulit Pisang untuk Mengurangi Penggunaan NBKP sebagai Bahan Baku Base Paper Baking Paper. JURNAL VOKASI TEKNOLOGI INDUSTRI (JVTI), 2(2).

Kamaluddin, M. A., Maryono, M., Hasri, H., & Rizal, H. P. (2022). Pengaruh Penambahan Plasticizer Terhadap Karakteristik Bioplastik dari Selulosa Limbah Kertas. Analit: Analytical and Environmental Chemistry, 7(02), 197-208.

Putri, F., Meidinariasty, A., & Yerizam, M. (2023). Pemanfaatan Limbah Ampas Tebu dan Alang-Alang pada Pembuatan Kertas Karton dengan Proses Pulping Organosolv. Jurnal Pendidikan Tambusai, 7(3), 22060-22068.

Ramadhany, P., & Handoko, T. (2021, October). Pengaruh Kandungan Selulosa dan Lignin pada Pulp Kulit Pisang Kepok dalam Pembuatan Kertas Seni. In Prosiding Seminar Nasional Riset dan Teknologi Terapan (Ritektra) (pp. D6-D6).

Amelia, A. N., Purnamasari, I., & Hasan, A. (2023). Laju Pengeringan Pulp Dari Campuran Tandan Kosong Kelapa Sawit dan Ampas Tebu Menggunakan Alat Tray Dryer. Jurnal Pendidikan Tambusai, 7(3), 21654-21660.

Aritonang, B., Ritonga, A. H., & Sinaga, E. M. (2019). Pemanfaatan Limbah Kulit Nenas Dan Ampas Tebu Sebagai Bahan Dasar Dalam Pembuatan Kertas Menggunakan Bahan Pengikat Pati Limbah Kulit Pisang Kepok. Jurnal Kimia Saintek dan Pendidikan, 3(2), 64-75.

KS, B. A., & Jumiati, E. (2023). ANALISIS SIFAT FISIS PEMBUATAN KERTAS DARI SERAT DAUN NANAS DAN KULIT DURIAN. Jurnal Kumparan Fisika, 6(2), 125-132.

Handayani, I., & Elfarisna, E. (2021). Efektivitas Penggunaan Pupuk Organik Cair Kulit Pisang Kepok Terhadap Pertumbuhan Dan Produksi Tanaman Pakcoy. Jurnal Agrosains dan Teknologi, 6(1), 25-34.

Thaib, C. M., Gultom, E., & Aritonang, B. (2020). Pembuatan Kertas Dari Limbah Kulit Durian dan Ampas Tebu Dengan Perbedaan Konsentrasi NaOH. JURNAL KIMIA SAINTEK DAN PENDIDIKAN, 4(1), 1-11.

Pulungan, A. H., Jumiati, E., & Lubis, R. Y. (2023). PENGARUH GRAMATUR TERHADAP DAYA REGANG PADA PEMBUATAN KERTAS BERBAHAN KULIT. JOURNAL ONLINE OF PHYSICS, 8(3), 99-103.

Oktaviananda, C., Purnavita, S., & Ayunindhia, S. D. (2023). PENGARUH WAKTU PEMASAKAN DAN PERSENTASE PVAc TERHADAP KUALITAS KERTAS DARI MAHKOTA NANAS. Jurnal Inovasi Teknik Kimia, 8(2), 127-132.

Hastuti, N., & Rahmayanti, H. D. (2022). Formulasi baru pembuatan kertas berbasis serat aren sebagai potensi material grafika di masa depan. Kreator, 9(2), 8-13.

Fiskia, E., & Mala, C. D. F. U. (2021). Formulasi Dan Evaluasi Sediaan Sabun Kertas Ekstrak Etanol Fuli Buah Pala (Myritica fragrans Houtt). Kieraha Medical Journal, 3(2), 120-127.

Sahdiah, H., & Kurniawan, R. (2023). Optimasi Tegangan Akselerasi pada Scanning Electron Microscope–Energy Dispersive X-Ray Spectroscopy (SEM-EDX) untuk Pengamatan Morfologi Sampel Biologi. Jurnal Sains dan Edukasi Sains, 6(2), 117-123.

DOI: https://doi.org/10.30596/rmme.v8i1.19480

Refbacks

There are currently no refbacks.

This work is licensed under a Creative Commons Attribution 3.0 License

Jurnal Rekayasa Material, Manufaktur dan Energi is abstracting & indexing in the following databases:

This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.

Statcounter View My Stats RMME