Pengaruh Variasi Tipe Sambungan Las SMAW pada Baja Karbon Rendah terhadap Uji Tarik dan Uji Impact

Rafidan Azimansyah, Nely Ana Mufarida, Mokh. Hairul Bahri

Abstract


This study was conducted to examine the effect  various fusing  joint types over the tensile force  and impact toughness of low carbon metal SS400 utilise Shielded Metal Arc Welding (SMAW) method. Three joint types were tested double Bevel groove, double V groove, double U groove, using 100A current and E6013 electrode with a diameter of 2,6 mm. The test were conducted at the state polytechnic of Malang. The tensile test results showed that the double Bevel joint had the highest tensil strength, with a maximum value of 11.626 Mpa. Meanwhile, the umpact test revealed the highest energy absorption at 127.468 Joules or 2.12 Joules/mm2 for the same joint type. The study concludes that the double Bevel groove joint provides the best mechanical performance for SS400 steel, making it the most recommended option for applications requiring high resistance to tensil and impact loads.

Keywords


SMAW Welding, SS400 Steel, Tensil Test, Impact Test

Full Text:

PDF

References


Agustus, V. N., Yaqin, M. A., & Mufarida, N. A. (2019). J-Proteksion PENGARUH VARIASI ARUS PENGELASAN SHIELD METAL ARC WELDING ( SMAW ) TERHADAP KEKUATAN TARIK PADA MATERIAL STAINLESS STEEL 304L The Effect of The Variation of Welding Current of Shield Metal Arc Welding ( SMAW ) on The Tensile Strength of Stain. 4(1), 8–10.

Chairul, N., Irzal, I., Mulianti, M., & Nurdin, H. (2022). Pengaruh Variasi Kuat Arus Terhadap Kekuatan Tarik Hasil Pengelasan Smaw Pada Baja Karbon Rendah Dengan Elektroda E-7018. Jurnal Vokasi Mekanika (VoMek), 4(4), 167–172. https://doi.org/10.24036/vomek.v4i4.470

Dikwan, M., Jokosisworo, S., & Zakki, A. F. (2019). JURNAL TEKNIK PERKAPALAN Pengaruh Normalizing Terhadap Kekuatan Tarik, Impak, dan Mikrografi Pada Sambungan Las Baja A36 Akibat Pengelasan Shielded-Metal Arc Welding (SMAW) dengan Variasi 2 waktu Pemanasan. Jurnal Teknik Perkapalan, 7(4), 440–448. https://ejournal3.undip.ac.id/index.php/naval

Famoesa, M. A. P., S, P. I., & Pranatal, E. (2020). Pengaruh variasi sudut kampuh v pada sambungan las fcaw dari material baja ss 400. E-Journal ITATS, 2(1), 85–93.

Hendaryati, H., & Mamungkas, M. I. (2021). Pengaruh Tipe Saluran Pengecoran Terhadap Sifat Mekanik Dan Struktur Mikro Aluminium Al 6061 Dengan Metode Sand Casting. Rotor, 14(2), 43. https://doi.org/10.19184/rotor.v14i2.22086

Las, S., Pada, T. I. G., & Alloy, A. (2022). Indra Eka Prasetya 1) , Kosjoko 2) , Nely Ana Mufarida 3). 9(1), 1–10. http://je.politala.ac.id

Mabrullah, R. A., Kosjoko, & Shofiyah, R. (2024). Pengaruh Variasi Arus pada Pengelasan SMAW terhadap Uji Kekuatan Bending dan Struktur Mikco Baja ST 42. Journal of Engineering Science and Technology , 2(2), 53–61.

Mahendra, Y., Lesmanah, U., & Basjir, M. (2022). Pengelasan SMAW dan GMAW Pada Baja SS400. Jurnal Unisma, 22–26.

Posisi, P., Terhadap, D. A. N., & Tarik, K. (2021). SAMBUNGAN LAS SMAW DENGAN MODEL KAMPUH V DAN KAMPUH X. 16(April), 14–17.

Purwanto, A., Wijoyo, W., & Fajar Riyadin, A. (2023). Pengaruh Polaritas Mesin Las pada Pengelasan SMAW (Shielded Metal Arc Welding) Terhadap Sifat Fisik dan Mekanik Baja Karbon Rendah. Jurnal Teknik Indonesia, 2(4), 150–158. https://doi.org/10.58860/jti.v2i4.238

Salahudin, X., Ihza, Y., Pramono, C., & Widodo, S. (2021). Analisis Kekuatan Tarik Baja Karbon Rendah Hasil Pengelasan Smaw Dengan Variasi Bentuk Kampuh Las. Journal of Mechanical Engineering, 5(1), 8–14. https://doi.org/10.31002/jom.v5i1.3941

Surahman, A., Mufarida, N. A., & ... (2023). Pengaruh Variasi Arus Las SMAW Terhadap Uji Tarik dan Uji Kekerasan Serta Struktur Mikro Pada Bahan ST 37. Journal of Engineering …, 1(3), 129–137. https://jesty.pubmedia.id/index.php/jesty/article/view/21%0Ahttps://jesty.pubmedia.id/index.php/jesty/article/download/21/18

Suwasono, B., Farizal, M., Nugroho, N. Y., & Hardianto, D. (2023). Identifikasi Kekuatan Butt Joint dan Lap Joint pada Pengelasan Konstruksi Kapal. Rekayasa, 16(2), 243–249. https://doi.org/10.21107/rekayasa.v16i2.19914

Teknologi, J. S., & Mikro, S. (2024). Pengaruh Variasi Jumlah Layer Las Smaw Material Aisi 1045 Terhadap Kekuatan Tarik dan Structur Micro The Effect of Variation in Number of Smaw Weld Layers of Aisi 1045 Material on Tensile Strength and Micro Structures. 6(1), 108–120.

Utomo, C. W., & Yunus, Y. (2021). Pengaruh posisi pengelasan terhadap kekuatan tarik dan tekuk pada sambungan Las Baja ST 41. Jurnal Teknik Mesin UNESA, 9(2), 1–4. https://ejournal.unesa.ac.id/index.php/jtm-unesa/article/view/39923




DOI: https://doi.org/10.30596/rmme.v8i2.24931

Refbacks





Creative Commons License

 This work is licensed under a Creative Commons Attribution 3.0 License

Jurnal Rekayasa Material, Manufaktur dan Energi  is abstracting & indexing in the following databases: 

  
 

Creative Commons License

This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.

Statcounter View My Stats RMME